perhitungan raw material kelompok 1
DESCRIPTION
Perhitungan Raw Mix Design pada Pabrik SemenTRANSCRIPT
1
PERHITUNGAN RAW MATERIAL
A. Data-data yang Digunakan
Komposisi Senyawa dalam Raw Material
Senyawa Batu Kapur
(L/S)
Tanah Liat
(C/L)
Pasir Slika
(S/S)
Pasir Besi
(I/S)
CaCO3 92.14% 14.82% 1.07% 6.25%
CaO 51.6% 8.3% 0.6% 3.5%
SiO2 1.70% 48.4% 85.0% 23.0%
Al2O3 0.80% 16.7% 4.0% 7.0%
Fe2O3 0.50% 7.2% 1.7% 60.0%
MgO 0.40% 1.8% 0.2% 1.5%
LiO 42.2% 10.0% 2.1% 0.0%
H2O 7.20% 30.0% 6.5% 8.4%
Persamaan Modulus
LSF = 100 CaO
2,8 SiO2 + 1,1 Al2O3 + 0,3 Fe2o3
SR = SiO2
Al2O3 + Fe2O3
AR = Al2O3
Fe2O3
Nilai Modulus Raw Material
LSF 105
SR 2
AR 1.35
Komposisi Raw Material Yang Berpengaruh Dalam Parameter
Senyawa L/S C/L S/S I/S
CaO 94.51% 10.30% 0.66% 3.74%
SiO2 3.11% 60.05% 93.10% 24.60%
Al2O3 1.47% 20.72% 4.38% 7.49%
Fe2O3 0.92% 8.93% 1.86% 64.17%
Total 100.00% 100.00% 100.00% 100.00%
2
B. Menentukan Raw Mix Design
Persen komposisi raw material diperoleh dari perhitungan menggunakan
solver excel, diperoleh data sebagai berikut:
Komponen Komposisi
Batu Kapur (L/S) 70.51939%
Tanah Liat (C/L) 21.59202%
Pasir Silika (S/S) 5.20511%
Pasir Besi (I/S) 2.68348%
Variasi Kadar CaO dalam Batu Kapur
- Range kadar CaO dalam batu kapur = 51.6% - 53.4%
- Interval yang dipilih = 0.2%
Berdasarkan modulus yang telah ditetapkan dan perhitungan menggunakan
solver diperoleh:
Variasi
CaO
Batu kapur
(L/S)
Tanah liat
(C/L)
Pasir silika
(S/S)
Pasir besi
(I/S)
51.6% 70.51938% 21.59208% 5.20507% 2.68347%
51.8% 70.50418% 21.60607% 5.20613% 2.68361%
52.0% 70.48910% 21.61996% 5.20719% 2.68375%
52.2% 70.47413% 21.63375% 5.20823% 2.68389%
52.4% 70.45927% 21.64743% 5.20927% 2.68403%
52.6% 70.44453% 21.66100% 5.21031% 2.68417%
52.8% 70.42958% 21.67580% 5.21133% 2.68432%
53.0% 70.41411% 21.69310% 5.21234% 2.68449%
53.2% 70.39970% 21.70637% 5.21335% 2.68462%
53.4% 70.38540% 21.71955% 5.21434% 2.68475%
3
C. Data dalam Bentuk Grafik
Gambar 1 Hubungan Variasi Kadar CaO Batu Kapur dengan Komposisi Raw
Material
0%
10%
20%
30%
40%
50%
60%
70%
80%
51.6% 51.8% 52.0% 52.2% 52.4% 52.6% 52.8% 53.0% 53.2% 53.4%
% b
erat
variasi kadar CaO
Hubungan Variasi Kadar CaO dengan Komposisi
Raw Meterial
L/S
C/L
S/S
I/S
4
Gambar 2 Hubungan Variasi Kadar CaO dengan Persen Berat Batu Kapur
Gambar 3 Hubungan Variasi Kadar CaO dengan Persen Berat Tanah Liat
70.30%
70.35%
70.40%
70.45%
70.50%
70.55%
51.6% 51.8% 52.0% 52.2% 52.4% 52.6% 52.8% 53.0% 53.2% 53.4%
% b
erat
batu
kap
ur
variasi kadar CaO
Hubungan Variasi Kadar CaO dengan Persen Berat
Batu Kapur
21.50%
21.55%
21.60%
21.65%
21.70%
21.75%
51.6% 51.8% 52.0% 52.2% 52.4% 52.6% 52.8% 53.0% 53.2% 53.4%
% b
erat
tan
ah
lia
t
variasi kadar CaO
Hubungan Variasi Kadar CaO dengan Persen Berat
Tanah Liat
5
Gambar 3 Hubungan Variasi Kadar CaO dengan Persen Berat Pasir Besi
Gambar 3 Hubungan Variasi Kadar CaO dengan Persen Berat Pasir Silika
2.683%
2.683%
2.684%
2.684%
2.685%
2.685%
51.6% 51.8% 52.0% 52.2% 52.4% 52.6% 52.8% 53.0% 53.2% 53.4%
% b
erat
pasi
r b
esi
variasi kadar CaO
Hubungan Variasi Kadar CaO dengan Persen Berat
Pasir Besi
5.200%
5.202%
5.204%
5.206%
5.208%
5.210%
5.212%
5.214%
5.216%
51.6% 51.8% 52.0% 52.2% 52.4% 52.6% 52.8% 53.0% 53.2% 53.4%
% b
erat
pasi
r si
lik
a
variasi kadar CaO
Hubungan Variasi Kadar CaO dengan Persen Berat
Pasir Silika
6
KESIMPULAN
1. Berubahnya kadar CaO dalam batu kapur dengan nilai modulus yang tetap
menyebabkan komposisi raw material berubah.
2. Dari data diperoleh kecenderungan persen komposisi batu kapur menurun
dengan bertambahnya kadar CaO, sedangkan persen komposisi tanah liat,
pasir silika, dan pasir besi meningkat.