proses manufaktur 7

7/23/2019 PROSES MANUFAKTUR 7

1/21

EXTRUSIONDEPARTEMEN TEKNIK INDUSTRIUNIVERSITAS SUMATERA UTARA


2/21

EXTRUSION ADALAH PROSES PENEKANANBILLET BERBENTUK SILINDER SEHINGGAMELEWATI/MELALUI CETAKAN DANBENTUKNYA AKAN MENGIKUTI CETAKAN

SELAMA PROSES EXTRUSION MATERIALMENGALAMI GAYA KOMPRES/TEKAN TRIAXIAL,MATERIAL MENGALAMI DEFORMASI YANGBESAR TANPA FRACTURE

BEBERAPA PRODUK TERCIPTA MELALUIPROSES INI REL PINTU SORONG, RANGKA

JENDELA, GEAR, HANGERS DAN SEBAGAINYA.

ALUMUNIUM, COPPER, STEEL DANMAGNESIUM ADALAH MATERIAL YANG SERING

INTRODUCTION


3/21


4/21

CONTOH PRODUK

EXTRUSION


5/21

PROSES EXTRUSI BERGANTUNG KEPADATINGKAT DUCTILITY MATERIAL EXTRUSI DAPAT DILAKUKAN PADA

TEMPERATUR RUANG DAN TEMPERATURTINGGI DRAWING ADALAH PROSES PENGURANGAN

LUAS AREA ATAU PEMBENTUKAN WIRE,

TUBING, SOLID ROD DENGAN MENARIKMELALUI CETAKAN.

INTRODUCTION


6/21

ADA TIGA TIPE PROSES EXTRUSI YAITU DIRECT EXTRUSI DIMANA PENEMPATAN BILLET

DIDALAM CHAMBER/CONTAINER DANKEMUDIAN DITEKAN OLEH HYDRAULIK AM

HINGGA BILLET MELALUI CETAKAN. INDIRECT EXTRUSI (REVERSE, BACKWARD)

DIMANA CETAKAN BERGERAK SEPANJANGBILLET UNTUK MENGURANGI LUAS AREANYA.

LATERAL (SIDE) EXTRUSI DIMANA BILLETBERADA DALAM POSISI VERTIKAL DANMENDAPAT PENEKANAN DARI ATAS.

PROSES EXTRUSI


7/21

PROSES EXTRUSI


8/21

VARIABEL GEOMETRI DALAM PROSES EXTRUSIADALAH SUDUT CETAKAN DAN RASIO LUAS AREABILLET SEBELUM DAN SESUDAH DIEXTRUSI (R)

VARIABEL LAIN YANG MEMPENGARUHI PROSES

EXTRUSI ADALAH TEMPERATUR BILLET, KECEPATANHIDRAULIK RAM DAN LUBRICANT YANG DIGUNAKAN.

GAYA YANG DIBUTUHKAN DALAM PROSES EXTRUSIBERGANTUNG KEPADA STRENGTH BILLET, RASIOEXTRUSI DAN GESEKAN ANTARA BILLET DANCONTAINER DAN BILLET DENGAN CETAKAN

F AO! L" (AO/ A#)

PROSES EXTRUSI


9/21

PROSES EXTRUSI


10/21

NILAK k


11/21

SEBUAH BILLET TERBUAT DARI $%&'% BRASSDI EXTRUSI PADA TEMPERATUR $%%%C.DIAMETER BILLET ADALAH * ++ DANDIAMETER SETELAH EXTRUSI ADALAH *%++. HITUNGLAH GAYA YANG DIBUTUHKAN.

CONTOH PERHITUNGAN


12/21

NILAI ! SETELAH MELIHAT GAMBAR ADALAH*% M- MAKA GAYA YANG DIBUTUHKANADALAH

F (*)/ 0 (*%) L" ((*) /(*%)) F *.1 MN


13/21

METAL FLOW PADA PROSES EXTRUSI AKANMEMPENGARUHI KUALITAS DANMECHANICAL PROPERTI DARI PRODUKEXTRUSI.

POLA ALIRAN DIBENTUK SESUAI PRINSIPENERGY DIKURANGI DALAM SETIAP PROSES.

METAL FLOW MEMBENTUK LONGITUDINAL

SEHINGGA PRODUK EXTRUSI AKANMEMBENTUK PERPANJANGAN GRAINSTRUKTUR

STRUKTUR MATERIAL PADA

PROSES EXTRUSI


14/21


15/21

DALAM PRAKTEKNYA R BIASANYA ANTARA%&%%.

PANJANG PRODUK EXTRUSI BIASANYAKURANG DARI $.* +

KECEPATAN RAM 2 % SAMPAI DENGAN %.*+/3

SUDUT MATA CETAKAN DAPAT MEMBENTUK

SISA MATERIAL YANG TERTINGGAL DICHAMBER.

PROSES PARAMETER


16/21

UNTUK METAL DAN ALLOY YANG TIDAK MEMILIKITINGKAT DUCTILITY YANG BAIK/CUKUP DALAMTEMPERATUR RUANG, MAKA PROSES EXTRUSIDILAKUKAN PADA TEMPERATUR TINGGI.

HOT EXTRUSI DAPAT MENYEBABKANKERUSAKAN PADA CETAKAN, PENDINGINANPERMUKAAN HOT BILLET DAN MENGHASILKANNON UNIFORM DEFORMATION

AKIBAT PEMANASAN PADA BILLET AKANMENIMBULKAN OXIDE FILM PADA PERMUKAANBILLET

HOT EXTRUSI


17/21

S4UARE DESAIN DIGUNAKAN UNTUKMENGEXTRUSI NON FERROUS METAL TERUTAMAUNTUK ALUMUNIUM.

TUBING DIEXTRUSI DAN MEMBENTUK SOLID

ATAU BILLET YANG BERONGGA. DIMANAMANDREL AKAN LENGKET PADA HIDRAULIK RAM.

UNTUK MEMBENTUK RONGGA DAPATMENGGUNAKAN METODE WELDING CHAMBER

METHOD ATAU MENGGUNAKAN VARIASI CETAKANSEPERTI SPIDER DIE, PORTHOLE DIE DAN BRIDGEDIE.

DESAIN CETAKAN


18/21

DESAIN CETAKAN


19/21

DESAIN CETAKAN


20/21

DESAIN CETAKAN


21/21

MATERIAL UNTUK HOT EXTRUSI ADALAHHOT WOR DIE STEEL YANG DI COATINGDENGAN 5IRCONIA.

LUBRIKASI AKAN MEMBERIKAN EFEK KEPADAALIRAN MATERIAL, SURFACE FINISH,KUALITAS PRODUK DAN GAYA EXTRUSI.

GLASS ADALAH LUBRIKAN YANG COCOK

UNTUK STEEL, STAILEES STEEL DAN HIGHTEMPERATURE METAL.

MATERIAL CETAKAN DAN

LUBRIKASI